Quality Assurance
Tested Against the Highest Standards
Every KENMOS product undergoes rigorous evaluation to meet stringent performance and durability benchmarks. Our testing ensures reliable results across all
In wall
| Test Items | Standard Indicators | Test Value | Individual Determinant |
|---|---|---|---|
| Coating Thickness | Least value ≥16 μm | 29 μm (Average 30 μm) | Consilient |
| Glossiness Deviation |
≤ 10(gloss < 70pm) ≤ 5(gloss ≥ 70pm) |
2.6 (gloss 24.0) | Consilient |
| Pencil Hardness | ≥ HB | 3H | Consilient |
| Coating Flexibility | ≤ 3T | 1T | Consilient |
| Adhesion | No Inferior to Grade 1 | Graticule Grade 0/Cycle Grade 1 | Consilient |
| Impact Resistance | 50kg. cm/No paintstripping, No cracks | 50kg. cm/No paintstripping, No cracks | Consilient |
| Boiling Water Resistance | Unconverted | Unconverted | Consilient |
| Acid Resistance | Unconverted | Unconverted | Consilient |
| Alkaline Resistance | Unconverted | Unconverted | Consilient |
| Oil Resistance | Unconverted | Unconverted | Consilient |
| Impregnant Resistance | Unconverted | Unconverted | Consilient |
| Rinse Resistance | Unconverted by ≥ 10000 times | Unconverted by ≥ 10000 times | Consilient |
| Surface Density | ± 0.5kg/m² | 5.32kg/m² | Consilient |
| Flexural Strength | ≥ 60 Mpa | 79.6Mpa | Consilient |
| Bending Elastic Modulus | ≥ 1.5 × 10⁴ Mpa | 1.99×10⁴Mpa | Consilient |
| Cross-Resistance | ≥ 5.0KN | 6.25KN | Consilient |
| Shear Strength | ≥ 20.0Mpa | 22.6Mpa | Consilient |
| 180° Peel Strength | ≥ 5.0N/mm | 6.2 N/mm | Consilient |
| Temperature Resistance | Unconverted | Unconverted | Consilient |
| Heat Distortion Temperature | ≥ 95°C | 116° C | Consilient |
| Thermal Expansion Coefficient | ≤ 4.00×10⁻⁵ °C⁻¹ | 2.74×10⁻⁵ °C⁻¹ | Consilient |
In wall
| Test Items | Standard Indicators | Test Value | Individual Determinant |
|---|---|---|---|
| Coating Thickness | Least value ≥16 μm | 29 μm (Average 30 μm) | Consilient |
| Glossiness Deviation |
≤ 10(gloss < 70pm) ≤ 5(gloss ≥ 70pm) |
2.6 (gloss 24.0) | Consilient |
| Pencil Hardness | ≥ HB | 3H | Consilient |
| Coating Flexibility | ≤ 3T | 1T | Consilient |
| Adhesion | No Inferior to Grade 1 | Graticule Grade 0/Cycle Grade 1 | Consilient |
| Impact Resistance | 50kg. cm/No paintstripping, No cracks | 50kg. cm/No paintstripping, No cracks | Consilient |
| Boiling Water Resistance | Unconverted | Unconverted | Consilient |
| Acid Resistance | Unconverted | Unconverted | Consilient |
| Alkaline Resistance | Unconverted | Unconverted | Consilient |
| Oil Resistance | Unconverted | Unconverted | Consilient |
| Impregnant Resistance | Unconverted | Unconverted | Consilient |
| Rinse Resistance | Unconverted by ≥ 10000 times | Unconverted by ≥ 10000 times | Consilient |
| Surface Density | ± 0.5kg/m² | 5.32kg/m² | Consilient |
| Flexural Strength | ≥ 60 Mpa | 79.6Mpa | Consilient |
| Bending Elastic Modulus | ≥ 1.5 × 10⁴ Mpa | 1.99×10⁴Mpa | Consilient |
| Cross-Resistance | ≥ 5.0KN | 6.25KN | Consilient |
| Shear Strength | ≥ 20.0Mpa | 22.6Mpa | Consilient |
| 180° Peel Strength | ≥ 5.0N/mm | 6.2 N/mm | Consilient |
| Temperature Resistance | Unconverted | Unconverted | Consilient |
| Heat Distortion Temperature | ≥ 95°C | 116° C | Consilient |
| Thermal Expansion Coefficient | ≤ 4.00×10⁻⁵ °C⁻¹ | 2.74×10⁻⁵ °C⁻¹ | Consilient |